PC and PC Alloy

Item	Test Standard	Unit	Typical Performance
Item	Test Standard	Unit	C500	C1000	CT1000	CS1000	C1304	CS500	CT500	CT302	CT306
Density	D792	g/cm³	1.20	1.25	1.30	1.22	1.35	1.45	1.55	1.28	1.38
Tensile Strength	D638	MPa	60	70	60	60	75	100	120	70	90
Elongation at Break	D638	%	60	3	3	10	2	2	2	3	3
Bending Strength	D790	MPa	90	100	90	90	120	160	200	80	100
Flexural Modulus	D790	MPa	2400	2500	2500	2500	3500	5000	8000	3000	4500
Notched Impact Strength of Cantilever	D256	kJ/㎡	50.0	10.0	15.0	20.0	6.0	6.0	6.0	8.0	12.0
Rockwell Hardness, HRR	D785	——	105	110	115	115	118	120	120	120	120
Melting Point		℃	——	——	——	——	——	——	——	——	——
Heat Distortion Temperature, 0.45MPa	D648	℃	120	135	150	140	200	215	220	225	230
Flame Retardance	UL94	Grade	V2	V0	V0	V0	HB	HB	HB	HB	HB
Surface Resistance	D257	Ω	10¹⁴	10¹⁴	10¹⁴	10¹⁴	10¹³	10¹³	10¹³	10¹³	10¹³
Dielectric Strength	D149	KV/mm	16	16	16	15	15	20	20	20	20
Mould Shrinkage	D955	mm/mm	0.006	0.005	0.006	0.006	0.006	0.006	0.012	0.008	0.004
Filling Amount		%	——	——	——	——	GF20	——	——	GF10	GF30
Features			General type	General flame retardant type			Glass fiber reinforced flame retardant type	Alloy		Glass fiber reinforced alloy
Use			Electronics	Electronics connector			Electronic components	Mobile telephone shell, meter case, bumper, auto parts		Mechanical parts